Process for making lithium transition metal phosphate powder for battery electrode

ABSTRACT

Methods of manufacture and use of phosphates of transition metals are described as positive electrodes for secondary lithium batteries, including a process for the production of LiMPO 4  with controlled size and morphology, M being Fe x Co y Ni z Mn w , where 0≦x≦1, 0≦y≦1, 0≦w≦1, and x+y+z+w=1. According to an exemplary embodiment, a process is described for the manufacture of LiFePO 4  including the steps of providing an equimolar aqueous solution of Li 1+ , Fe 3+  and PO 4   3− , evaporating water from the solution to produce a solid mixture, decomposing the solid mixture at a temperature of below 500° C. to form a pure homogeneous Li and Fe phosphate precursor, and annealing the precursor at a temperature of less than 800° C. in a reducing atmosphere to produce the LiFePO 4  powder. The obtained powders can have a particle size of less than 1 μm, and can provide superior electrochemical performance when mixed for an appropriate time with an electrically conductive powder.

This application is a divisional of U.S. application Ser. No. 10/719,134, filed Nov. 21, 2003, now U.S. Pat. No. 7,371,482 which application is a continuation application under 35 U.S.C. §120 of International Application No. PCT/EP02/05714 filed May 22, 2002, which designated the United States and was published in English; and which International Application claims benefit of priority under 35 U.S.C. 119(a)-(d) and/or §365 to European Patent Application No. 01401374.2 filed May 23, 2001; the entire contents of each of these applications being incorporated herein by reference.

Lithium secondary batteries are now widely used in consumer electronics. They benefit from the light weight of lithium and from its strong reducing character, thus providing the highest energy density among known rechargeable battery systems. Lithium secondary batteries exist in various configurations depending on the nature of the electrode materials and of the electrolyte used. Commercialised Li-ion system use for instance LiCoO₂ and graphite respectively as positive and negative electrodes, with LiPF₆ in EC/DEC/PC as a liquid electrolyte. The operating voltage of the battery is related to the difference between thermodynamic free energies within the negative and positive electrodes. Solid oxidants are therefore required at the positive electrode, the materials of choice, up to now, being either the layered LiMO₂ oxides (M is Co or Ni) or the 3-dimensional spinel structure of LiMn₂O₄. Extraction of lithium from each of these three oxides gives access to M⁴⁺/M³⁺ redox couples located between 4 and 5 V vs. Li⁺/Li.

Three-dimensional structures using (XO₄)^(n−) polyanions instead of simple oxides have been proposed recently by J. B. Goodenough et al. in U.S. Pat. No. 5,910,382 as viable alternatives to LiM_(x)O_(y) oxides. In particular, LiFePO₄ and Li₃Fe₂(PO₄)₃ were said to be the most promising Fe-containing materials working at attractive potentials of 3.5 V and 2.8 V respectively vs. Li⁺/Li. Both compounds operate with the Fe³⁺/Fe²⁺ redox couple and take advantage of the inductive effect of the XO₄ ^(n−) groups that diminishes the strength of the Fe—O bond compared to a simple oxide.

Padhi et al. in J. Elec. Soc. 144(4) demonstrated the reversible extraction of lithium from olivine LiFePO₄ prepared at relatively high temperatures of 800° C. under Ar atmosphere from a solid/solid mixture of Li₂CO₃ or LiOH.H₂O, Fe(CH₃COO)₂ and NH₄H₂PO₄.H₂O. The products used in the solid/solid reaction are costly, especially Fe(CH₃COO)₂, and this process leads to LiFePO₄ particles of large average size, typically more than 30 μm. Only 60 to 70% of the theoretical capacity of 170 mAh/g was achieved at a very low charge/discharge rate of around C/80. Less capacity is to be expected at higher current densities of e.g. C/5.

Several authors reported improvements in the effective reversible capacity of LiFePO₄. This was attained through various synthesis strategies that involved either the coating of electronic conductive carbon on LiFePO₄ particles (N. Ravet et al., Proc. Elec. Soc. Meeting, Hawai, 1999) or the use of strongly reactive Fe^(II) oxalate as a precursor for obtaining LiFePO₄ particles at moderate temperatures (Ri et al. in JP-2000-294238 or Yamada et al. in Elec. Soc. 148(3), A224 (2001)). The Fe^(II) oxalate precursor route described in JP-2000-294238 is a solid/solid reaction that requires extensive grinding/mixing of the NH₄H₂PO₄, FeC₂O₄ and Li₂CO₃ precursors in acetone and evaporation under N₂. This step is followed by a thermal treatment at temperatures ranging from 300 to 790° C. The particle size obtained in this case was also around 30 μm.

In the prior art, Fe^(II) is selected as a starting product for the synthesis of LiFePO₄. The synthesis is realised under inert (Ar or N₂) atmosphere so as to avoid the oxidation of Fe^(II) to Fe^(III). However, Fe^(II) sources either are very expensive, e.g. Fe^(II) acetate, or may lead to the formation of strongly toxic gases, e.g. CO during the thermal decomposition of Fe^(II) oxalate. Moreover, these Fe^(II) precursors are prone to oxidation into Fe^(III) in air and must be handled under inert atmosphere or under a non-aqueous solvent. Also, particle sizes of at least 30 μm were obtained and such course grain sizes lead to kinetic limitations, in particular when high charge/discharge rates are applied at ambient temperatures such as 25° C.

Another problem in the effective use of LiFePO₄ as a positive electrode arises from its low electronic conductivity and from the fact that both LiFePO₄ and FePO₄ are poor ionic conductors. Therefore, a certain amount of electronic conductive powder, such as Acetylene Black, has to be intermixed with the lithium transition-metal phosphate powder. In the case of JP-2000-294238, the LiFePO₄/Acetylene Black ratio was 70/25. Such a high content of electrical conducting agent penalises the overall specific capacity of the composite positive electrode.

It is an object of the present invention to overcome at least some of the disadvantages of the above mentioned processes and products. The present invention discloses a new synthesis technique based on the use of components that may be dissolved in water to yield, after decomposition and annealing under inert or reducing atmosphere, LiMPO₄ of controlled particle size.

A process for the manufacture of a LiMPO₄ powder is disclosed, comprising the steps of

-   -   providing an equimolar aqueous solution of Li¹⁺, M^(n+) and PO₄         ³⁻ prepared by dissolving components which are susceptible to         coexist as solutes in an aqueous system and which, upon heating         at a temperature below 500° C., decompose to form a pure         homogeneous Li and M phosphate precursor,     -   evaporating the water from the solution, thereby producing a         solid mixture,     -   decomposing the solid mixture at a temperature below 500° C. to         form a pure homogeneous Li and M phosphate precursor, and     -   annealing the precursor at a temperature of less than 800° C.,         in an inert or reducing atmosphere, thereby forming a LiMPO₄         powder, whereby M^(n+) is one or more of Fe²⁺, Fe³⁺, Co²⁺, Ni²⁺         and Mn²⁺, and M is Fe_(x)Co_(y)Ni_(z)Mn_(w), with 0≦x≦1, 0≦y≦1,         0≦z≦1, 0≦w≦1 and x+y+z+w=1. Preferentially, in the step of         annealing the precursor, the annealing temperature is less than         600° C.

In another embodiment of the invention, a process is disclosed for the manufacture of a LiFePO₄ powder, comprising the steps of

-   -   providing an equimolar aqueous solution of Li¹⁺, Fe³⁺ and PO₄ ³⁻         prepared by dissolving components which are susceptible to         coexist as solutes in an aqueous system and which, upon heating         at a temperature below 500° C., decompose to form a pure         homogeneous Li and Fe phosphate precursor,     -   evaporating the water from the solution, thereby producing a         solid mixture,     -   decomposing the solid mixture at a temperature below 500° C. to         form a pure homogeneous Li and Fe phosphate precursor, and     -   annealing the precursor Li and Fe phosphate at a temperature of         less than 800° C. in a reducing atmosphere, thereby forming a         LiFePO₄ powder. Preferentially, in the step of annealing the         precursor, the annealing temperature is less than 600° C.

In this embodiment the invention allows the use of cheap and abundant Fe^(III) starting products such as Fe(NO₃)₃.9H₂O or any other iron nitrate, to produce LiFePO₄. It should be appreciated that the reduction of Fe^(III) to Fe^(II) can be completed by a short annealing step at relatively low temperatures in a reducing atmosphere, thereby ensuring that only limited grain growth occurs. It is believed that the high reactivity of the solid mixture is due to the extreme homogeneity obtained by the process according to the invention. In the solid/solid reactions according to the prior art however, it is difficult to start from Fe^(III) bearing products, because the reduction of Fe^(III) to Fe^(II) necessitates a lengthy annealing step at high temperature (e.g. 24 hrs at 700-800° C.), resulting in coarse particles with poor electrochemical characteristics and possible reduction of Fe^(II) to Fe metal.

The invention also concerns a powder for use in lithium insertion-type electrodes with formula LiMPO₄ having an average particle size of less than 1 μm, whereby M is Fe_(x)Co_(y)Ni_(z)Mn_(w) with 0≦x≦1, 0≦y≦1, 0≦z≦1, 0≦w≦1; x+z+w>0, and x+y+z+w=1. Such a product can be obtained by controlling the temperature of the annealing step of the decomposed solid mixture. The small particle size allows achieving high reversible capacities at high current densities and at 25° C., which were not previously observed.

The invention further concerns a powder for use in lithium secondary batteries, having the formula LiFePO₄, and characterised by a reversible electrode capacity of at least 65% of the theoretical capacity, when used as an active component in a cathode which is cycled between 2.70 and 4.15 V vs. Li⁺/Li at a discharge rate of C/5 at 25° C.

The invention further concerns a process for the manufacture of a lithium insertion-type electrode comprising the steps of

-   -   providing a mixture of a lithium metal phosphate powder         synthesised according to the invention, and a conductive carbon         bearing powder, and     -   milling this mixture during a period of time so as to optimise         the reversible electrode capacity of the electrode comprising         said mixture.

In particular, the invention concerns the above lithium insertion-type electrode, whereby the lithium metal phosphate powder is LiFePO₄, the conductive carbon powder is acetylene black or CARBON SUPER P, the mixing ratio of LiFePO₄/carbon is between 75/25 and 85/15, and the milling time is between 15 and 25 minutes.

The present invention also provides a positive electrode material, LiMPO₄ (M is Fe_(x)Co_(y)Ni₂Mn_(w), with 0≦x≦1, 0≦y≦1, 0≦z≦1, 0≦w≦1 and x+y+z+w=1) for use in rechargeable battery systems comprising an electrolyte, a negative electrode and a separator between the two electrodes.

The details of the invention are illustrated in FIGS. 1 to 11.

FIG. 1 is the X-ray diffraction pattern of LiFePO₄ according to the invention.

FIG. 2 shows a microphotograph of LiFePO₄ obtained by solid/solid reaction at 800° C. according to prior art.

FIGS. 3 (a) to (d) shows microphotographs of LiFePO₄ according to the invention and annealed at 500, 600, 700 and 800 C.° respectively.

FIG. 4 is the potential (V) vs. x (intercalation in Li_(x)FePO₄) behaviour of LiFePO₄ according to the invention, annealed at 500° C., mixed with CARBON SUPER P for 20 minutes and measured at C/5 and 25° C.

FIG. 5 shows the influence of the milling time (min.) of LiFePO.sub.4 powder according to the invention with CARBON SUPER P on the electrochemical capacity (mAh/g) of the obtained electrode material.

FIG. 6 is a comparison of the potential (V) vs. x (intercalation in Li_(x)FePO₄) behaviour of LiFePO₄ obtained by solid/solid reaction at 800° C. according to prior art, (A) without and (B) with further grinding.

FIG. 7 shows a microphotograph of the further ground powder used for obtaining the results shown in FIG. 6(B).

FIG. 8 is the potential (V) vs. x (intercalation in Li_(x)FePO₄) behaviour of LiFePO₄ according to the invention, annealed at 500° C. and measured at C/50 and 25° C.

FIG. 9 is the potential (V) vs. x (intercalation in Li_(x)FePO₄) behaviour of LiFePO₄ according to the invention, annealed at 500° C. and measured at C/5 and 55° C.

FIG. 10 is the potential (V) vs. x (intercalation in Li_(x)FePO₄) behaviour of LiFePO₄ according to the invention, annealed at 500° C. and measured at C/5 and 80° C.

FIG. 11 shows the influence of the number of cycles (N) on an electrode containing LiFePO₄ powder according to the invention on the electrochemical charge (C+) and discharge (C−) capacity (mAh/g) of the obtained electrode material.

For the preparation of LiFePO₄, an aqueous solution of a 1 M Fe(NO₃)₃.9H₂O is in a first step slowly added under stirring in air to an equal quantity of a 1 M aqueous solution of LiH₂PO₄ (synthesised from Li₂CO₃ and H₃PO₄) at a pH between 3 and 4. In a second step, the water is slowly evaporated in a known way between 80 and 175° C. in air, to produce a very homogeneous precursor mixture containing Li, Fe and P in the stoichiometric proportions of LiFePO₄. More concentrated solutions can be used successfully without penalty towards the purity of the powder produced. The homogeneous precursor that contains Fe^(III) is annealed for 5 to 15 hours in a N₂/H₂ reducing atmosphere with e.g. 10% H₂ at a temperature of at least 500° C. to yield a pure crystalline LiFePO₄ phase. One or two intermediate grindings can be applied during annealing to allow complete reduction of the Fe^(III) into Fe^(II). Small amounts of Fe^(III), preferably not exceeding 5 mole %, can be tolerated in the final product.

The X-ray diffraction pattern of powder obtained according to above process and annealed at 500° C. is shown in FIG. 1. The diffraction peaks are indexed in the orthorhombic space group Pmnb of the olivine LiFePO₄ with unit-cell parameters of a=6.004 Å, b=10.326 Å and c=4.691 Å.

FIG. 2 shows the geometry of a particle of LiFePO₄ prior art powder obtained at 800° C. through solid state reaction of Fe(CH₃COO)₂, Li₂CO₃ and NH₄H₂PO₄ under Ar. The powder is characterised by an average particle size of about 50 μm and by a specific surface of less than 0.5 m²/g.

The LiFePO₄ powder obtained by the process of the invention as illustrated in the example above is characterised by a small average particle size of less than 1 μm and a specific surface of 2 to 3 m²/g. Adjustment of the particle size and of the specific surface can be obtained by controlling the annealing temperature between 500 and 800° C. The invention provides thus an easy way of producing LiFePO₄ particles of desired sizes and morphologies. As can be seen in FIG. 3( a) to (d), increasing the annealing temperature results in a progressive increase in particle size and consequently in a decrease of the specific surface. Table 1 summarises the results.

TABLE 1 Influence of the annealing temperature on particle size and specific surface area. Annealing temperature (° C.) 500 600 700 800 Average particle size (μm) <1 μm 1 μm 5 μm 25 μm Specific surface (m²/g) 2.84 1.06 0.54 0.30

The LiFePO₄ powder may be used effectively as a positive electrode in an electrochemical cell. Prior to the cell realisation, an intimate mixture of LiFePO₄ together with conducting carbon, preferably acetylene black or CARBON SUPER P, is produced. To this end, LiFePO₄ and carbon are introduced in the commonly used weight ratio of 83/17 in a stainless steel vessel, preferably filled with Ar, and ball milled for an adequate time with a milling apparatus such as a SPEX-8000. The LiFePO₄ particles are hereby coated with conductive carbon. Adding a binder for cell operation is not mandatory. The electrochemical characteristics of LiFePO₄ prepared by the process according to the invention are evaluated in a Swagelok cell configuration with lithium metal pasted on a nickel foil as the negative electrode and LiPF₆ in EC/DMC as the electrolyte. The electrochemical characteristics of LiFePO₄ as a function of the charge/discharge rate and of the temperature were evaluated.

LiFePO₄ particles were produced at an annealing temperature of 500° C. according to the invention, and milled with CARBON SUPER P (available from MMM Carbon, Belgium) in a weight ratio of 83/17 for 20 minutes. The obtained powder behaves very well at a high charge/discharge rate of C/5, i.e. one lithium extracted or inserted within 5 hours: as can be seen in FIG. 4, 67% of the theoretical value of 170 mAh/g is observed, which equals to a reversible capacity of 114 mAh/g.

FIG. 5 shows a graph with the relationship between milling time of LiFePO₄ particles with CARBON SUPER P and the reversible capacity obtained. It can be observed that the milling time has a considerable influence and that an optimum milling time can be established, e.g. in the range of between 15 and 25 minutes for the SPEX-8000 milling apparatus.

The positive electrode of the invention may be used in either Li-ion type batteries with carbon at the negative electrode and a non-aqueous liquid electrolyte, or, when operating at 80° C., in polymer-type batteries with metallic lithium at the negative electrode and a POE-type polymer as the electrolyte. When M is Co, Ni or Mn, the use is restricted to non-aqueous liquid electrolyte systems, providing that the electrolyte used is stable at the high operating voltage of more than 4 V of the cell.

As an illustration of the improvements achieved by the invention, the particles of a prior art LiFePO₄ powder as shown in FIG. 2, i.e. obtained at 800° C. from a solid state reaction under Ar of Fe(CH₃COO)₂, Li₂CO₃ and NH₄H₂PO₄, were mixed with Carbon Super P in a weight ratio of 83/17 and tested in an electrochemical cell built in the Swagelok configuration. The positive electrode composite was deposited directly on the aluminium current collector. The electrochemical response of the powder is given in FIG. 6(A). The characteristic voltage curves as a function of x in Li_(x)FePO₄ were obtained at equivalent charge/discharge rate of C/5 and 25° C. As can be seen, during charge/discharge cycling less than 40% of the theoretical capacity is reached.

It is essential to realise that further grinding of the particles of a prior art LiFePO₄ powder does not lead to powders obtainable by the low-temperature synthesis of the invention which are characterised by small particles. Indeed, extensive grinding of the prior art LiFePO₄ particles did not result in efficient comminution. This can be seen by comparing FIG. 2, showing a typical prior art LiFePO₄ particle before further grinding, and FIG. 7, showing a typical prior art LiFePO₄ particle after 90 minutes of grinding and 15 minutes of milling with carbon using a SPEX-8000 milling apparatus.

Moreover, amorphisation of the powder, and thus loss of the electrochemical activity of the olivine LiFePO₄, occurs during grinding: FIG. 6(B) indeed shows that the relative capacity degrades from less than 40% before grinding to 15% after grinding. Note that in this experiment, the milling time with carbon was also observed to be a critical parameter. The reported capacities correspond to those obtained after optimal milling.

For the composite electrode prepared with LiFePO₄ synthesised according to the invention at an annealing temperature of 500° C. and mixed in a 83/17 weight ratio with Carbon Super P, the effects of the cycling regime and of the temperature on the observed charge and discharge behaviour are summarised in FIGS. 8 to 10. As can be seen in FIG. 8, the slow kinetics of the front-type reaction between LiFePO₄ and FePO₄ are less penalising at a slower charge/discharge rate, as a reversible electrode capacity of 80% of the theoretical capacity for a charge/discharge rate of C/50 is observed. Also, as illustrated in FIGS. 9 and 10, the kinetics improve with increasing operating temperature of the electrochemical cell. A reversible capacity as high as 90% of the theoretical capacity is reached at 80° C. Moreover, it is remarkable to observe the very small polarisation of the electrochemical cell under these conditions.

Finally, tests have shown the high stability of LiFePO₄, even when cycled at a relatively high temperature of 55° C., as is demonstrated in FIG. 11. The cycling was performed at charge and discharge rates of C/10.

LiCoPO₄ can also be synthesised according to the invented process. To this end, an aqueous solution of a 1 M Co(NO₃)₂.6H₂O is in a first step slowly added under stirring in air to an equal quantity of a 1 M aqueous solution of LiH₂PO₄ at a pH between 3 and 4. In a second step, the water is slowly evaporated in a known way at 95° C. in air, to produce a very homogeneous precursor mixture containing Li, Co and P in the stoichiometric proportions of LiCoPO₄. The homogeneous precursor that contains Li, Co^(II) and P is annealed for 10 hours in an inert N₂ atmosphere at a temperature of 500° C. to yield a pure crystalline LiCoPO₄ phase. One intermediate grinding is applied during annealing in order to enhance the homogeneity of the final product. 

1. A process for the manufacture of a lithium insertion electrode comprising the steps of: providing an equimolar aqueous solution of Li¹⁺, M^(n+) and PO₄ ³⁻ prepared by dissolving components which are susceptible to coexist as solutes in an aqueous system and which, upon heating at a temperature below 500° C., decompose to form a pure homogeneous Li and M phosphate precursor; evaporating water from the solution, thereby producing a solid mixture; decomposing the solid mixture at a temperature below 500° C. to form a pure homogeneous Li and M phosphate precursor; annealing the precursor at a temperature of less than 600° C. in an inert or reducing atmosphere, thereby forming a LiMPO₄ powder of olivine structure; providing a mixture of the LiMPO₄ powder and a conductive carbon bearing powder; and milling the mixture during a period of time to optimize the reversible capacity of the electrode thereby producing a lithium insertion electrode; wherein M^(n+) is one or more of Fe²⁺, Fe³⁺, Co²⁺, Ni²⁺ and Mn²⁺ and M is Fe_(x)Co_(y)Ni_(z)Mn_(w), with 0≦x≦1, 0≦y≦1, 0≦z≦1, 0≦w≦1, and x+y+z+w=1.
 2. The process according to claim 1, wherein M is Fe, the weight ratio of LiFePO₄/carbon is between 75/25 and 85/15, and the milling time is between 15 and 25 minutes.
 3. The process according to claim 1, wherein the LiMPO₄ powder has an average particle size of less than 1 μm and x+z+w>0.
 4. The process according to claim 3, wherein M is Fe and the reversible electrode capacity is at least 65% of a theoretical capacity when used as an active component in a cathode that is cycled between 2.70 and 4.15 V vs. Li⁺/Li at a discharge rate of C/5 at 25° C.
 5. The process according to claim 2, wherein the conductive carbon powder is acetylene black. 